PROPERTIES |
SAE
J 1703
Requirement |
D.O.T.
3
Requirement |
D.O.T.
4
Requirement |
Equilibrium
Reflux Boiling point
Wet E.R. Boiling Point
Viscosity at - 40°C
Viscosity at + 100°C
Ph Value
|
°C
°C
cS
cS |
|
min.
205
-
max. 1800
min. 1.5
7,0 - 11,5 |
min.
205
min. 140
max. 1500
min. 1.5
7,0 - 11,5
|
min.
205
min. 155
max. 1800
min. 1.5
7,0 - 11,5 |
High
Temperature Stability E.R. Boiling Point
Change
|
°C
|
Chemical
Stability Temperature Decrease
|
°C
|
|
max.
3 + 0,05
for each degree
ERBP > 225
max. 2,0 |
max.
3 + 0,05
for each degree
ERBP > 225 |
max.
3 + 0,05
for each degree
ERBP > 225 |
max.
3 + 0,05
for each degree
ERBP > 225 |
max.
3 + 0,05
for each degree
ERBP > 225 |
Corrosion
Metal Strips/Weight Change mg/cm²
Tinned
Iron
Steel
Aluminium
Cast
Iron
Brass
Copper
Fluid-Water
Mixture
Sediment
pH
Rubber Cups
Hardness
Decrease
Base
Diameter Increase |
|
|
max. 0,2
max. 0,2
max. 0,1
max. 0,2
max. 0,4
max. 0,4
max.
0,10
7,0 - 11,5
max.
15
max. 1,4 |
max. 0,2
max. 0,2
max. 0,1
max. 0,2
max. 0,4
max. 0,4
max.
0,10
7,0 - 11,5
max.
15
max. 1,4 |
max. 0,2
max. 0,2
max. 0,1
max. 0,2
max. 0,4
max. 0,4
max.
0,10
7,0 - 11,5
max.
15
max. 1,4 |
Fluidity
and Appearance Low Temperature
At - 40°C Discernibility Black Contrast
Lines
Stratification
or Sedimentation
Air
Bubble Travel Time
At - 50°C Discernibility Black Contrast
Lines
Stratification
or Sedimentation
Air
Bubble Travel Time
|
Sec
Sec
|
|
Clearly
None
max.10
Clearly
None
max. 35 |
Clearly
None
max.10
Clearly
None
max. 35 |
Clearly
None
max.10
Clearly
None
max. 35 |
Evaporation
Weight Loss
Gritty or Abrasive Precipate in Residue
Pourpoint of Residue |
%
°C
|
|
max. 80
None
max. -5 |
max. 80
None
max. -5 |
max. 80
None
max. -5 |
| Water
Tolerance |
-40°C
+60°C |
Discernibility Contrast Lines
Stratification or Sedimentation
Air Bubble Travel Time
Stratification or
Sedimentation |
Sec
Vol. % |
|
| |
Clearly
None
max.10
None
max. 0,15 |
|
| |
Clearly
None
max.10
None
max. 0,15 |
|
| |
Clearly
None
max.10
None
max. 0,15 |
|
| Compatibility |
-40°C
+60°C |
Discernibility Contrast Lines
Stratification or Sedimentation
Stratification or
Sedimentation |
Vol. % |
|
| |
Clearly
None
None
max. 0,05 |
|
| |
Clearly
None
None
max. 0,05 |
|
| |
Clearly
None
None
max. 0,05 |
|
| Resistance
to Oxidation |
Metal
Strips
Weight Change |
Pitting or Roughening
Pitting or Etching
Gum Deposit
Aluminium Strip
Cast Iron Strip |
mg/cm³
mg/cm³ |
|
|
| |
-
None
Trace
max. 0.05
max 0,3 |
|
| |
-
None
Trace
max. 0.05
max 0,3 |
|
| Effect
on SBR Cups |
+70°C
+120°C |
Hardness Increase
Hardness Decrease
Disintegration
(Stickinessblisters, sloughing)
Base Diameter Increase
Hardness Increase
Hardness Decrease
Disintegration
(Stickinessblisters, sloughing)
Base Diameter Increase
|
IRHDegrees
mm
IRHDegrees
mm |
|
| |
None
max. 10
None
0,15 - 1,40
None
max. 15
None
0,15 - 1,40 |
|
| |
None
max. 10
None
0,15 - 1,40
None
max. 15
None
0,15 - 1,40 |
|
| |
None
max. 10
None
0,15 - 1,40
None
max. 15
None
0,15 - 1,40 |
|